The Influence of Solid-State Polycondensation of Polyethylene Terephthalate on Its Rheological Properties

ENG: The influence of solid-state polycondensation conditions on the rheological properties of polyethylene terephthalate was determined. Mathematical models describing the dependence of the melt flow rate of both virgin and recycled polyethylene terephthalate on the time and temperature of the solid-state polycondensation process were developed. A correlation between the melt flow rate and the average molecular weight of polyethylene terephthalate was demonstrated. Experimental studies showed that conducting solid-state polycondensation of recycled polyethylene terephthalate at temperatures ranging from 130 оC to 160 оC for 3 hours produces polymeric materials with higher molecular weight and, consequently, improved performance properties.

UKR: Встановлено вплив умов перебігу процесів твердофазної поліконденсації поліетилентерефталату на його реологічні властивості. Розроблено математичні моделі залежностей показника текучості розплаву первинного та вторинного поліетилентерефталату від часу та температури проведення його твердофазної поліконденсації. Показана кореляція між показником текучості розплаву та показником середньої молекулярної маси поліетилентерефталату. На підставі здійснених експериментальних досліджень встановлено, що проведення твердофазної поліконденсації вторинного поліетилентерефталату (при температурі від 130 оС до 160 оС протягом 3 годин) дозволяє одержувати полімерні матеріали з більш високою молекулярною масою і, відповідно, з підвищеним рівнем експлуатаційних властивостей.